9A SOLID FILM LUBRICANT
HEAT CURING
SERIES E750
MEETS SAE SPEC AS5272C Type II
FORMERLY MIL-L-46010D TYPE II
TECHNICAL INFORMATION GUIDE
.
Lubricative Pigment Molybdenum Disulfide
Color Flat Dark Gray
Shelf Life 1 year from date of Manufacture
Vacuum Outgassing None @ 10-6 Torr.
Lox Compatibility 100% compatible and shock resistant
Resistivity 1.4 x 106 OHMS CM
Coefficient of Friction 0.0236 (Falex Test)
Load Carrying Capacity 2250 lbs. ASTM D2625 B
Corrosion Protection OVER 1500 hours* ASTM B117
(@ .0005" DFT on DoD-P-16232 Type M
Class 3 phosphated steel)
*Test halted before failure occurred
COMPOSTITON AND PHYSICAL PROPERTIES
DESCRTPTION
Sandstrom 9A Dry Film Lubricant is a paint-like coating
containing molybdenum disulfide and corrosion inhibiting
pigments. This Heat Curing material prevents corrosion,
galling, seizing, and fretting. It is a low-friction coating which
exhibits long wear life when operated at -3200F to +5000F
under loads exceeding 100,000 psi.
9A should be applied where maximum wear life and corrosion
protection from a dry film lubricant are required.
Once Sandstrom 9A has been heat cured, it is virtually
unaffected by atmospheric and fretting corrosion, solvents,
acids, oils, degreasers, and is not resoftened again at elevated
temperatures.
9A can be applied to a wide variety of surfaces by spraying
or dipping. Complete application instructions are on the
reverse of this sheet.
OUTSTANDING FEATURES/BENEFITS
Excellent Corrosion Protection, Chemical Resistance, and
Long Wear Life are its outstanding characteristics.
SANDSTROM 9A CONTAINS NO GRAPHITE
Use Sandstrom "099" as an alternative to 9A where low VOC
and no lead is preferred. 099's performance is comparable