華北S211銅焊絲

Category

類 別

Trade
mark

牌 號

Chemical composition

主要成份(%)

Characteristics & application

特性和用途

Equivalent to AWS

相當(dāng)AWS

Hardfacing

硬

面

堆

焊

S 101

C3 Cr28 Ni4
Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54，耐磨、耐氣蝕、抗氧化。堆焊鏟斗齒，泵套

S 111

C1 Cr29 W5
Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47，高溫下耐磨、耐蝕。堆焊高溫高壓閥門

ECoCr-A

S 112

C1.5 Cr29 W8
Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50，高溫下耐磨、耐蝕。堆焊閥門，熱軋孔型

ECoCr-B

S 113

C2.5 Cr30 W17
Co Rem.

HRc≥55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc≥55，高溫下耐磨、耐熱，但抗沖擊性差。堆焊螺旋送料機(jī)用

S 114

C2.5 Cr30 W12
Co Rem.

HRc≥53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc≥53，高溫下耐磨、耐熱，但抗沖擊較差。堆焊牙輪鉆頭

ECoCr-C

Copper

alloys

銅

合

金

S 201

Sn1 Si0.3Mn0.3
Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
機(jī)械性能好，抗裂性好。紫銅氣焊及氬弧焊用

ERCu

S 211

Si3 Mn1
Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
機(jī)械性能好，銅合金氬弧焊及鋼的MIG釬焊用

ERCuSi-Al

S 212

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。銅合金氬弧焊及鋼的堆焊用

ERCuSn-A

S 213

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。銅合金氬弧焊及鋼的堆焊用

ERCuSn-C

S 214

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用

ERCuAl-A1

S 215

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蝕。銅合金氬弧焊及鋼的堆焊用

ERCuAl-A2

S 221

Cu60 Sn1 Si0.3
Zn Rem.

Melting point is about 890℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點(diǎn)約890℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

S 221F

Cu60 Sn1 Si 0.3
Zn Rem.

S221 welding rod coated with flux.
外涂焊劑的S221焊絲

S 222

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點(diǎn)約880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

RBCuZn-C

S 222F

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

S222 welding rod coated with flux.
外涂焊劑的S222焊絲

RBCuZn-C

S 223

Cu59 Sn0.6
Zn Rem.

Melting point is about 900℃. Braze welding of copper, steel and cast iron.
熔點(diǎn)約900℃。銅、鋼、鑄鐵釬焊用

RBCuZn-A

S 224

Cu62 Si0.5
Zn Rem.

Melting point is about 905℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點(diǎn)約905℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

Copper
alloys

銅

合

金

S 225

Cu48 Ni10
Zn Rem.

Melting point is about 935℃ and high strength. Braze welding of steel, nickel and carbide alloys.
熔點(diǎn)約935℃。高強(qiáng)度,釬焊鋼、鎳及硬質(zhì)合金用

RBCuZn-D

S 225F

Cu48 Ni10
Zn Rem.

S225 welding rod coated with flux.
外涂焊劑的S225焊絲

RBCuZn-D

S 226

Cu60 Sn0.3
Si0.2 Zn Rem.

Melting point is about 900℃. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔點(diǎn)約900℃。黃銅氣焊用，也可釬焊銅、鋼、鑄鐵

S 227

Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.

Melting point is about 880℃. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔點(diǎn)880℃。黃銅氣焊及碳弧焊用，也可釬焊銅、鋼、鑄鐵

RBCuZn-B

S 229

Cu55 Ni6 Mn4
Zn余

Melting point is about 920℃, high strength. Braze welding of steel, nickel and hard carbide.
熔點(diǎn)約920℃。高強(qiáng)度,釬焊鋼、鎳及硬質(zhì)合金用

Aluminum alloys

鋁

合

金

S 301

Al≥99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蝕。純鋁氣焊、氬弧焊用

ER1100

S 311

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好，通用性大。鋁合金氣焊、氬弧焊用。不宜用高鎂合金

ER4043

S 321

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蝕性、可焊性及塑性。鋁合金氣焊、氬弧焊用

S 331

Mg5 Mn0.4
Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蝕，強(qiáng)度高。鋁合金氬弧焊用

ER5183