進(jìn)口MWA工模具之H13鋼焊條Mac Tool E3064硬度53-60HRC

英國進(jìn)口MWA工模具焊條MAC TOOL E3064|H13工具鋼

A low hydrogen, iron powder basic flux coated electrode. Designed for special hardfacing applications involving heavy impact loading combined with abrasion. This electrode is ideally suited for forging dies because of its very tough deposit. It is an H13 type product. Pre-heat and dilution may effect hardness on first two layers but not on subsequent layers. On heavy build-ups use Mac Trode E6718 as buffer layer on carbon steels and Mac Trode E630 on 13% manganese steels

Mac Tool E3064為低氫鐵粉堿性焊劑涂層焊條，專為涉及劇烈沖擊載荷和磨損的特殊硬面堆焊應(yīng)用而設(shè)計(jì)。該款焊條熔覆層非常堅(jiān)硬、耐高溫性能佳，特別適合錘鍛模。它是H13型產(chǎn)品。預(yù)熱和稀釋可能會(huì)影響前兩層的硬度，但不會(huì)影響后續(xù)熔敷層的硬度。對(duì)于厚堆焊，在碳鋼上使用Mac Trode E6718 作為緩沖層，在13%錳鋼上使用Mac Trode E630。

1. Resists Heavy Impact. 抗劇烈沖擊。
2. Ideal for Hammer Dies. 非常適合錘鍛模。
3. Good High Temperature Resistance. 良好的耐高溫性。
4. Weld Deposit Matches H13 Steel. 熔敷層與H13鋼匹配。
5. Weld Metal Hardness 50-56HRC. 焊縫金屬硬度50-56HRC。

Typical All Weld Metal Chemical Analysis (%)

典型全焊縫金屬成分

Typical All Weld Deposit Hardness

典型全焊縫金屬熔敷層硬度：

1st Layer第一層：53-55HRC(560-600HV)

2nd Layer第二層：56-60HRC(620-680HV)

3rd Layer第三層：57-60HRC(640-680HV)

Sizes Available and Recommended Amperages

尺寸Φ/電流：

Current電流：AC/DC?(+) AC (OCV 70 amps)

Related Specification參考標(biāo)準(zhǔn)：H13 Tool Steel

Storage儲(chǔ)存：Electrodes should be stored in dry conditions. Should the electrodes ?become damp, re-dry for one hour at 180°C before use. 焊條應(yīng)儲(chǔ)存在干燥環(huán)境中。如果焊條受潮，應(yīng)在180°C下重新干燥1小時(shí)后再使用。