碳鋼焊條
| 型號 | AWS | 熔敷金屬化學成分(%) | 熔敷金屬機械性能 | 用 途 | ||||||||||||
| C | Mn | Si | S | P | Cr | Ni | Mo | V | 其它 |
R m (MPa) |
Rel或Rp0.2 (MPa) |
A (%) |
A KV (J) |
|||
| E5015 | E7015 |
— 0.082 |
≤1.60 1.18 |
≤0.75 0.53 |
≤0.020 0.010 |
≤0.030 0.021 |
≤0.20 0.037 |
≤0.30 0.014 |
≤0.30 0.002 |
≤0.08 0.010 |
≥490 570 |
≥400 470 |
≥22 30 |
-30℃ ≥27 170 |
焊接中碳鋼及16Mn等較重要低合金鋼 | |
| E5016 | E7016 |
— 0.069 |
≤1.60 1.11 |
≤0.75 0.53 |
≤0.020 0.007 |
≤0.030 0.020 |
≤0.20 0.037 |
≤0.30 0.013 |
≤0.30 0.002 |
≤0.08 0.010 |
≥490 550 |
≥400 440 |
≥22 31 |
-30℃ ≥27 170 |
焊接中碳鋼及較重要低合金鋼 | |
| E5018 | E7018 |
— 0.068 |
≤1.60 1.08 |
≤0.75 0.41 |
≤0.020 0.012 |
≤0.030 0.015 |
≤0.20 0.011 |
≤0.30 0.035 |
≤0.30 0.001 |
≤0.08 0.002 |
≥490 560 |
≥400 465 |
≥22 29 |
-30℃ ≥27 160 |
碳鋼和相應強度的低合金鋼的高效率焊接 | |
| E5018-1 | E7018-1 |
— 0.075 |
≤1.60 1.00 |
≤0.75 0.40 |
≤0.020 0.010 |
≤0.030 0.015 |
≤0.20 0.012 |
≤0.30 0.030 |
≤0.30 0.001 |
≤0.08 0.001 |
≥490 560 |
≥400 470 |
≥22 30 |
-50℃ ≥27 110 |
碳鋼和相應強度的低合金鋼的高效率焊接 | |
| E5015HIC | E7015 |
— 0.082 |
≤1.60 1.18 |
≤0.75 0.53 |
≤0.010 0.006 |
≤0.010 0.009 |
≤0.20 0.008 |
≤0.30 0.014 |
≤0.30 0.002 |
≤0.08 0.010 |
≥490 570 |
≥400 470 |
≥22 30 |
-30℃ ≥27 170 |
適用于焊接16MnR(HIC)等鋼結構，如熱高溫分離器，循環氫分液罐等壓力容器或一些輸油管線焊接 | |
低合金鋼焊條
| 型號 | AWS | 熔敷金屬化學成分(%) | 熔敷金屬機械性能 | 用 途 | ||||||||||||
| C | Mn | Si | S | P | Cr | Ni | Mo | V |
R m (MPa) |
Rel或Rp0.2 (MPa) |
A (%) |
A KV (J) |
PWHT | |||
| E5015-G | E7015-G |
- 0.062 |
≥1.00 1.15 |
≥0.80 0.47 |
- 0.009 |
- 0.015 |
- |
≥0.50 0.70 |
- | - |
≥490 560 |
≥410 430 |
≥25 29 |
-40℃ ≥54 150 |
620℃×1h | 用于沖擊韌性有更高要求的壓力容器用低合金鋼的焊接 |
| E6015-G | E9015-G |
- 0.061 |
≥1.00 1.21 |
≥0.80 0.42 |
- 0.007 |
- 0.015 |
- |
≥0.50 0.95 |
≥0.20 0.26 |
- |
≥590 650 |
≥490 550 |
≥17 23 |
-50℃≥27 80 |
620℃×1h | 用于大型石油儲罐的焊接 |
| E5515-C1 | E8015-C1 |
≤0.12 0.040 |
≤1.25 0.95 |
≤0.60 0.35 |
≤0.035 0.012 |
≤0.035 0.015 |
- |
2.0-2.75 2.21 |
- | - |
≥540 580 |
≥440 490 |
≥17 30 |
-70℃≥27 110 |
620℃×1h | 用于-70℃低溫下2.5%Ni鋼的焊接 |
| E5018-A1 | E7018-A1 |
≤0.12 0.063 |
≤0.90 0.82 |
≤0.80 0.28 |
≤0.020 0.013 |
≤0.030 0.015 |
— | — |
0.40-0.65 0.57 |
— |
≥490 600 |
≥410 530 |
≥25 28 |
常溫≥27 170 |
620℃×1h | 用于工作溫度510℃以下的珠光體耐熱鋼焊接 |
| E5515-B2 | - |
0.05-0.12 0.067 |
≤0.90 0.70 |
≤0.60 0.37 |
≤0.020 0.011 |
≤0.030 0.015 |
0.80-1.50 1.14 |
— |
0.40-0.65 0.51 |
— |
≥550 630 |
≥460 510 |
≥19 24 |
常溫≥27 160 |
690℃×1h | 用于工作溫度520℃以下的珠光體耐熱鋼焊接 |
|
E5515-B2 (HIC) |
- |
0.05-0.12 0.055 |
≤0.90 0.80 |
≤0.60 0.28 |
≤0.020 0.006 |
≤0.030 0.009 |
0.80-1.50 1.27 |
— |
0.40-0.65 0.51 |
— |
≥550 640 |
≥460 500 |
≥19 25 |
-10℃ -30℃ ≥54 ≥54 200 100 |
690℃×8h | 適用于焊接工作在520℃以下的15CrMoR(HIC)等純凈度和力學性能要求高的耐熱鋼，如鍋爐管道、高壓容器、石油精煉設備等，也可用來焊接３０CrMnSi鑄鋼 |
| E5518-B2 | E8018-B2 |
0.05-0.12 0.080 |
≤0.90 0.73 |
≤0.80 0.24 |
≤0.020 0.009 |
≤0.030 0.013 |
0.80-1.5 1.31 |
— |
0.40-0.65 0.52 |
— |
≥540 630 |
≥440 520 |
≥19 22 |
常溫≥27 170 |
690℃×1h | 用于工作溫度520℃以下的1%鉻，0.5%鉬低合金鋼焊接 |
| E5515-B2-V | — |
0.05-0.12 0.066 |
≤0.90 0.70 |
≤0.60 0.37 |
≤0.020 0.012 |
≤0.030 0.015 |
0.8-1.5 1.12 |
— |
0.40-0.65 0.52 |
0.10-0.35 0.18 |
≥540 630 |
≥440 510 |
≥17 21 |
常溫≥27 150 |
730℃×2h | 用于工作溫度540℃以下的珠光體耐熱鋼焊接 |
| E6015-B3 | E9015-B3 |
0.05-0.12 0.067 |
≤0.90 0.65 |
≤0.60 0.38 |
≤0.020 0.012 |
≤0.030 0.016 |
2.00-2.50 2.23 |
— |
0.90-1.20 1.02 |
— |
≥590 680 |
≥490 570 |
≥17 20 |
常溫≥27 140 |
690℃×1h | 用于Cr2.25Mo珠光體耐熱鋼焊接 |
| E6018-B3 | E9018-B3 |
0.05-0.12 0.080 |
≤0.90 0.75 |
≤0.80 0.30 |
≤0.020 0.010 |
≤0.030 0.012 |
2.00-2.50 2.34 |
— |
0.90-1.20 1.14 |
— |
≥590 680 |
≥490 580 |
≥17 20 |
常溫≥27 180 |
690℃×1h | 用于Cr2.25Mo珠光體耐熱鋼焊接 |
不銹鋼焊條
|
牌號
|
AWS
|
熔敷金屬化學成分(%)
|
熔敷金屬力學性能
|
用 途
|
||||||||||
|
C
|
Mn
|
Si
|
S
|
P
|
Cr
|
Ni
|
Mo
|
Cu
|
其它
|
R m
(MPa) |
A
(%) |
|||
|
E5MoV-15
|
—
|
≤0.12
0.074 |
0.5-0.9
0.68 |
≤0.50
0.42 |
≤0.030
0.010 |
≤0.030
0.019 |
4.5-6.0
5.3 |
—
|
0.40-0.70
0.55 |
≤0.5
0.052 |
V : 0.10-0.35
0.25 |
≥540
625 (750℃×4h) |
≥14
20 (750℃×4h) |
用于Cr5MoV等珠光體耐熱鋼的焊接
|
|
E410-15
|
E410-15
|
≤0.12
0.048 |
≤1.0
0.81 |
≤0.90
0.44 |
≤0.030
0.007 |
≤0.030
0.023 |
11.0-13.5
13.16 |
≤0.70
0.51 |
≤0.75
0.12 |
≤0.75
0.15 |
—
|
≥450
545 (750℃×1h) |
≥20
23 (750℃×1h) |
用于0Cr13、1Cr13鋼和耐磨耐蝕鋼的表面堆焊
|
|
E410NiMo-15
|
E410NiMo-15
|
≤0.06
0.030 |
≤1.0
0.71 |
≤0.90
0.26 |
≤0.030
0.006 |
≤0.030
0.016 |
11.0-12.5
12.15 |
4.0-5.0
4.39 |
0.40-0.70
0.45 |
≤0.75
0.17 |
—
|
≥760
890 (610℃×1h) |
≥15
17 (610℃×1h) |
用于0Cr13不銹鋼焊接
|
|
E308-16
|
E308-16
|
≤0.08
0.052 |
0.5-2.5
1.33 |
≤0.90
0.71 |
≤0.030
0.007 |
≤0.030
0.021 |
18.0-21.0
19.82 |
9.0-11.0
9.45 |
≤0.75
0.13 |
≤0.75
0.20 |
—
|
≥550
630 |
≥35
40 |
用于工作溫度低于300℃的0Cr19Ni9不銹鋼結構的焊接
|
|
E308-15
|
E308-15
|
≤0.08
0.057 |
0.5-2.5
1.35 |
≤0.90
0.41 |
≤0.030
0.007 |
≤0.030
0.021 |
18.0-21.0
19.78 |
9.0-11.0
9.75 |
≤0.75
0.15 |
≤0.75
0.20 |
—
|
≥550
630 |
≥35
40 |
用于工作溫度低于300℃的0Cr19Ni9不銹鋼結構的焊接
|
|
E308H-16
|
E308H-16
|
0.04-0.08
0.058 |
0.5-2.5
1.14 |
≤0.90
0.62 |
≤0.030
0.007 |
≤0.030
0.020 |
18.0-21.0
19.70 |
9.0-11.0
9.68 |
≤0.75
0.20 |
≤0.75
0.10 |
—
|
≥550
645 |
≥35
42 |
用于工作溫度低于300℃的0Cr19Ni9不銹鋼結構的焊接
|
|
E308L-16
|
E308L-16
|
≤0.04
0.028 |
0.5-2.5
1.15 |
≤0.90
0.70 |
≤0.030
0.010 |
≤0.030
0.019 |
18.0-21.0
19.25 |
9.0-11.0
9.49 |
≤0.75
0.10 |
≤0.75
0.13 |
—
|
≥520
590 |
≥35
44 |
用于超低碳00Cr19Ni10或0Cr18Ni10Ti不銹鋼的焊接
|
|
E308L-16W
|
E308L-16
|
≤0.04
0.029 |
0.5-2.5
2.14 |
≤0.90
0.53 |
≤0.030
0.010 |
≤0.030
0.019 |
18.0-21.0
19.25 |
9.0-11.0
10.2 |
≤0.75
0.10 |
≤0.75
0.13 |
—
|
≥520
590 |
≥35
44 -196℃ A KV 41(J) |
用于超低碳00Cr19Ni10或0Cr18Ni10Ti不銹鋼的焊接,在196℃下有良好的韌性，適用于LNG儲罐及管道的焊接。
|
|
E309-16
|
E309-16
|
≤0.15
0.068 |
0.5-2.5
1.15 |
≤0.90
0.62 |
≤0.030
0.011 |
≤0.030
0.026 |
22.0-25.0
24.44 |
12.0-14.0
12.42 |
≤0.75
0.19 |
≤0.75
0.20 |
—
|
≥550
635 |
≥25
33 |
同類型不銹鋼及異種鋼的焊接
|
|
E309-15
|
E309-15
|
≤0.15
0.070 |
0.5-2.5
1.21 |
≤0.90
0.52 |
≤0.030
0.009 |
≤0.030
0.021 |
22.0-25.0
24.15 |
12.0-14.0
12.60 |
≤0.75
0.13 |
≤0.75
0.11 |
—
|
≥550
620 |
≥25
35 |
同類型不銹鋼及異種鋼的焊接
|
|
E309Mo-16
|
E309Mo-16
|
≤0.12
0.053 |
0.5-2.5
1.22 |
≤0.90
0.63 |
≤0.030
0.012 |
≤0.030
0.023 |
22.0-25.0
23.53 |
12.0-14.0
13.46 |
2.0-3.0
2.24 |
≤0.75
0.20 |
—
|
≥550
645 |
≥25
35 |
用于耐硫酸介質腐蝕的同類型不銹鋼焊接及異種鋼的焊接
|
|
E309MoL-16
|
E309MoL-16
|
≤0.04
0.029 |
0.5-2.5
1.05 |
≤0.90
0.54 |
≤0.030
0.009 |
≤0.030
0.021 |
22.0-25.0
23.23 |
12.0-14.0
12.65 |
2.0-3.0
2.21 |
≤0.75
0.15 |
—
|
≥540
630 |
≥25
34 |
用于相同類型的超低碳不銹鋼材料（如尿素合成塔襯里）及異種鋼焊接
|
|
E309L-16
|
E309L-16
|
≤0.04
0.033 |
0.5-2.5
1.23 |
≤0.90
0.65 |
≤0.030
0.009 |
≤0.030
0.021 |
22.0-25.0
24.40 |
12.0-14.0
12.70 |
≤0.75
0.10 |
≤0.75
0.15 |
—
|
≥520
610 |
≥25
37 |
用于相同類型的不銹鋼及復合鋼板、異種鋼焊接
|
|
E310-16
|
E310-16
|
0.08-0.20
0.13 |
1.0-2.5
1.89 |
≤0.75
0.41 |
≤0.030
0.009 |
≤0.030
0.020 |
25.0-28.0
27.31 |
20.0-22.5
21.40 |
≤0.75
0.12 |
≤0.75
0.10 |
—
|
≥550
650 |
≥25
34 |
焊接高溫條件下工作的同類型不銹鋼、異種鋼的焊接，如Cr5Mo、Cr9Mo、Cr13等
|
|
E310-15
|
E310-15
|
0.08-0.20
0.14 |
1.0-2.5
1.79 |
≤0.75
0.36 |
≤0.030
0.008 |
≤0.030
0.017 |
25.0-28.0
27.46 |
20.0-22.5
21.35 |
≤0.75
0.10 |
≤0.75
0.10 |
—
|
≥550
625 |
≥25
36 |
焊接高溫條件下工作的同類型不銹鋼及異種鋼的焊接，如Cr5Mo、Cr9Mo、Cr13等
|
|
E310Mo-16
|
E310Mo-16
|
≤0.12
0.081 |
1.0-2.5
1.72 |
≤0.75
0.39 |
≤0.030
0.011 |
≤0.030
0.020 |
25.0-28.0
26.91 |
20.0-22.0
20.99 |
2.0-3.0
2.45 |
≤0.75
0.10 |
—
|
≥550
660 |
≥25
36 |
焊接高溫條件下工作的同類型不銹鋼及異種鋼的焊接。
|
|
E312-16
|
E312-16
|
≤0.15
0.085 |
0.5-2.5
1.21 |
≤0.90
0.77 |
≤0.030
0.011 |
≤0.030
0.022 |
28.0-32.0
29.59 |
8.0-10.5
9.17 |
≤0.75
0.15 |
≤0.75
0.12 |
—
|
≥660
795 |
≥22
24 |
用于異種鋼的焊接
|
|
E316-16
|
E316-16
|
≤0.08
0.039 |
0.5-2.5
1.22 |
≤0.90
0.65 |
≤0.030
0.012 |
≤0.030
0.025 |
17.0-20.0
19.21 |
11.0-14.0
11.96 |
2.0-3.0
2.41 |
≤0.75
0.13 |
—
|
≥520
580 |
≥30
41 |
用于焊接在有機和無機酸介質中工作的0Cr18Ni12Mo2鋼
|
|
E316-15
|
E316-15
|
≤0.08
0.050 |
0.5-2.5
1.21 |
≤0.90
0.45 |
≤0.030
0.010 |
≤0.030
0.021 |
17.0-20.0
18.58 |
11.0-14.0
12.00 |
2.0-3.0
2.30 |
≤0.75
0.14 |
—
|
≥520
595 |
≥30
40 |
用于焊接在有機和無機酸介質中工作的0Cr18Ni12Mo2鋼
|
|
E316L-16
|
E316L-16
|
≤0.04
0.029 |
0.5-2.5
1.23 |
≤0.90
0.60 |
≤0.030
0.011 |
≤0.030
0.019 |
17.0-20.0
19.20 |
11.0-14.0
11.43 |
2.0-3.0
2.27 |
≤0.75
0.14 |
—
|
≥490
580 |
≥30
41 |
用于焊接尿素及合成纖維設備
|
|
E317L-16
|
E316L-16
|
≤0.04
0.029 |
0.5-2.5
1.23 |
≤0.90
0.60 |
≤0.030
0.011 |
≤0.030
0.019 |
18.0-21.0
19.90 |
12.0-14.0
11.43 |
3.0-4.0
2.27 |
≤0.75
0.14 |
—
|
≥490
580 |
≥30
41 |
用于同類型不銹鋼的焊接，具有較強的抗點蝕和縫隙腐蝕的能力。
|
|
E318-16
|
E318-16
|
≤0.08
0.045 |
0.5-2.5
1.30 |
≤0.90
0.45 |
≤0.030
0.009 |
≤0.030
0.025 |
17.0-20.0
18.95 |
11.0-14.0
11.60 |
2.0-3.0
2.12 |
≤0.75
0.15 |
Nb: 6xC%-1.00
0.60 |
≥520
610 |
≥25
35 |
用于0Cr18Ni12Mo2Ti不銹鋼的焊接
|
|
E347-16
|
E347-16
|
≤0.08
0.045 |
0.5-2.5
1.08 |
≤0.90
0.66 |
≤0.030
0.011 |
≤0.030
0.025 |
18.0-21.0
19.95 |
9.0-11.0
9.51 |
≤0.75
0.15 |
≤0.75
0.10 |
Nb: 8xC%-1.00
0.54 |
≥520
615 |
≥25
32 |
用于焊接含鈦的0Cr19Ni9Ti不銹鋼結構
|
|
E347-15
|
E347-15
|
≤0.08
0.062 |
0.5-2.5
1.24 |
≤0.90
0.48 |
≤0.030
0.009 |
≤0.030
0.021 |
18.0-21.0
19. 88 |
9.0-11.0
9.48 |
≤0.75
0.12 |
≤0.75
0.10 |
Nb: 8xC%-1.00
0.61 |
≥520
630 |
≥25
31 |
用于焊接含鈦的0Cr19Ni9Ti不銹鋼結構
|
|
E347L-16
|
E347-16
|
≤0.04
0.032 |
0.8-2.5
1.25 |
≤0.90
0.63 |
≤0.020
0.009 |
≤0.030
0.017 |
18.0-21.0
19.10 |
9.0-11.0
9.95 |
≤0.50
0.11 |
≤0.20
0.13 |
Nb: 8xC%-1.00
0.52 |
≥520
620 |
≥30
38 |
用于熱壁加氫反應器內壁不銹鋼堆焊，表層鐵素體含量3～8%
|
|
E2209-16
|
E2209-16
|
≤0.04
0.028 |
0.5-2.0
1.67 |
≤0.90
0.60 |
≤0.030
0.011 |
≤0.030
0.025 |
21.5-23.5
22.84 |
8.5-10.5
9.73 |
2.5-3.5
3.15 |
≤0.75
0.10 |
N: 0.08-0.2
0.11 |
≥690
765 |
≥20
28 |
用于石化、水工行業同類型超低碳不銹鋼焊接
|
|
E16-25MoN-15
|
—
|
≤0.12
0.054 |
0.5-2.5
1.27 |
≤0.90
0.62 |
≤0.030
0.007 |
≤0.030
0.017 |
14.0-18.0
16.69 |
22.0-27.0
23.43 |
5.0-7.0
6.56 |
≤0.50
0.12 |
N≥0.1
0.15 |
≥610
685 |
≥30
38 |
低合金鋼、中合金鋼、異種鋼的焊接
|
|
E1-19-10Mn6-15
|
—
|
≤0.14
0.07 |
3.5-7.0
5.9 |
0.30-1.20
0.51 |
≤0.025
0.012 |
≤0.030
0.021 |
18.0-21.0
19.8 |
8.0-11.0
9.8 |
—
|
—
|
常溫 Akv≥72
130 |
≥540
640 |
≥25
31 |
用于焊接高強度鋼、裝甲鋼和異種的焊接如H617
|
|
E385-16
|
E385-16
|
≤0.03
0.22
|
1.0～2.5
2.10
|
≤0.75
0.45
|
≤0.020
0.006
|
≤0.030
0.022
|
19.5～21.5
20.79
|
24.0～26.0
25.22
|
4.2～5.2
4.9
|
1.2～2.0
1.38
|
—
|
≥520
630
|
≥30
35
|
用于904L鋼的焊接
|
堆焊焊條
| 型號 | AWS | 熔敷金屬化學成分(%) | 用 途 | ||||||||
| C | Mn | Si | S | P | Cr | Fe | 其它 | 硬度 | |||
| EDMn-A-16 | EFeMn-A |
≤1.10 0.51 |
11.00-16.00 12.30 |
≤1.30 0.98 |
— — |
— — |
— — |
余量 |
≤5.00 — |
HB ≥170 |
高錳鋼堆焊 |
| EDCr-A1-15 | — |
≤0.15 0.11 |
— — |
— — |
≤0.030 0.011 |
≤0.040 0.021 |
10.00-16.00 13.25 |
余量 |
≤2.50 — |
HRC ≥40 |
1Cr13閥門堆焊 |
| EDCr-B-15 | — |
≤0.25 0.16 |
— — |
— — |
— — |
— — |
10.00-16.00 12.87 |
余量 |
≤5.00 — |
HRC ≥45 |
2Cr13閥門堆焊 |
鑄鐵焊條
| 型號 | AWS | 熔敷金屬化學成分(%) | 用 途 | |||||||
| C | Mn | Si | S | P | Ni | Fe | 其它 | |||
| EZC | — |
2.00-4.00 2.19 |
≤0.75 0.60 |
2.5-6.5 3.4 |
≤0.10 0.009 |
≤0.15 0.04 |
— — |
余量 |
— — |
一般灰口鑄鐵件焊補 |
| EZNi-1 | ENi-C1 |
≤2.0 0.25 |
≤1.0 0.86 |
≤2.50 1.71 |
≤0.03 0.009 |
— — |
≥90 94.55 |
≤8.0 1.75 |
≤1.0 ≤1.0 |
重要灰口鑄鐵薄壁件和加工面焊補 |
| EZNiFe-1 | ENiFe-C1 |
≤2.0 0.11 |
≤2.50 0.95 |
≤4.0 1.83 |
≤0.03 0.012 |
— — |
45-60 52.5 |
余量 |
≤1.0 ≤1.0 |
重要灰口鑄鐵及球墨鑄鐵件焊補 |
鎳基合金焊條
| 型號 | AWS | 熔敷金屬化學成分(%) | 熔敷金屬機械性能 | 用 途 | |||||||||||||
| C | Mn | Fe | P | S | Si | Ti | Ni | Cu | Cr | Nb+Ta | Mo | ? 其它 |
R m (MPa) |
A (%) |
|||
| ENiCrFe-3 | ENiCrFe-3 |
≤0.10 0.04 |
5.0-9.5 6.80 |
≤10.0 6.0 |
≤0.03 0.01 |
≤0.015 0.01 |
≤1.0 0.40 |
≤1.0 0.20 |
≥59 68.10 |
≤0.50 0.10 |
13.0-17.0 16.0 |
1.0-2.5 2.0 |
— — |
≤0.50 |
≥550 625 |
≥30 39 |
用于耐熱耐蝕鎳基合金焊接,亦可用于異種鋼的焊接 |
| ENiCrMo-3 | ENiCrMo-3 |
≤0.10 0.030 |
≤1.0 0.60 |
≤7.0 5.00 |
≤0.03 0.01 |
≤0.02 0.01 |
≤0.75 0.40 |
— — |
≥55.0 59.0 |
≤0.50 0.03 |
20.0-23.0 22.10 |
3.15-4.15 3.70 |
8.0-10.0 8.80 |
≤0.50 |
≥760 800 |
≥30 34 |
主要用于鎳基合金的焊接，也可用于一些難焊合金、異種鋼的焊接及深冷鋼的焊接 |
|
品名 |
AWSA5.9-93 |
GB/T 17854-99 |
熔敷金屬化學成份之一例 |
|||||||
|
TIG |
MIG |
C |
Si |
Mn |
Cr |
Ni |
Mo |
其它 |
||
|
FY·302 |
ER302 |
H1Cr18Ni9 |
0.10 |
0.65 |
1.72 |
17.5 |
9. 3 |
- |
- |
|
|
FY·304 |
ER304 |
H0Cr18Ni9 |
0.072 |
0.55 |
1.72 |
18.50 |
9.30 |
- |
- |
|
|
FY·307 |
ER307 |
- |
0.070 |
0.47 |
3.95 |
20.40 |
9.65 |
- |
- |
|
|
FY·307Si |
ER307Si |
- |
0.080 |
0.82 |
6.85 |
18.87 |
8.32 |
0.27 |
- |
|
|
FY·308 |
ER308 |
H0Cr21Ni10 |
0.03 |
0.34 |
1.82 |
20.13 |
9.50 |
- |
- |
|
|
FY·308L |
ER308L |
H00Cr21Ni10 |
0.02 |
0.42 |
1.65 |
20.10 |
10.33 |
- |
- |
|
|
FY·309 |
ER309 |
H1Cr24Ni13 |
0.083 |
0.42 |
1.63 |
23.83 |
13.13 |
- |
- |
|
|
FY·309L |
ER309L |
H00Cr24Ni13 |
0.02 |
0.39 |
1.98 |
23.88 |
12.90 |
- |
- |
|
|
FY·309LSi |
ER309LSi |
- |
0.02 |
0.87 |
1.55 |
24.10 |
13.00 |
- |
- |
|
|
FY·310 |
ER310 |
H1Cr26Ni21 |
0.086 |
0.40 |
2.01 |
27.40 |
21.80 |
- |
- |
|
|
FY·316 |
ER316 |
H0Cr19Ni12Mo2 |
0.050 |
0.36 |
1.78 |
19.61 |
12.50 |
5.49 |
- |
|
|
FY·316L |
ER316L |
H00Cr19Ni12Mo2 |
0.025 |
0.42 |
1.91 |
19.10 |
12.58 |
2.57 |
- |
|
|
FY·316LSi |
ER316LSi |
- |
0.021 |
0.77 |
1.95 |
19.32 |
13.45 |
2.58 |
- |
|
|
FY·317 |
ER317 |
H0Cr19Ni14Mo3 |
0.048 |
0.45 |
1.86 |
19.41 |
14.23 |
3.51 |
- |
|
|
FY·317L |
ER317L |
H00Cr19Ni14Mo3 |
0.023 |
0.40 |
1.76 |
19.60 |
13.68 |
3.63 |
- |
|
|
FY·HlCrl8Ni9Ti |
- |
H1Cr18Ni9Ti |
0.087 |
0.86 |
1.58 |
18.47 |
10.20 |
- |
Ti:0.62 |
|
|
FY·321 |
ER321 |
H0Cr20Ni10Ti |
0.062 |
0.49 |
1.74 |
19.50 |
9.57 |
- |
Ti:0.82 |
|
|
FY·H0Cr21Ni10Ti |
- |
H0Cr21Ni10Ti |
0.057 |
0.41 |
1.86 |
20.31 |
9.72 |
- |
Ti:0.73 |
|
|
FY·H0Cr18Ni9Ti |
- |
H0Cr18Ni9Ti |
0.053 |
0.57 |
1.27 |
18.61 |
10.20 |
- |
Ti:0.59 |
|
|
FY·347 |
ER347 |
H0Cr20Ni10Nb |
0.030 |
0.41 |
1.61 |
20.37 |
9.90 |
- |
Nb:0.80 |
|
|
FY·410 |
ER410 |
H1Cr13 |
0.100 |
0.45 |
0.43 |
11.81 |
0.17 |
- |
- |
|
|
FY·430 |
ER430 |
H1Cr17 |
0.038 |
0.39 |
0.46 |
16.37 |
0.20 |
- |
- |
|
|
FY·H2Cr13 |
- |
H2Cr13 |
0.160 |
0.45 |
0.51 |
13.00 |
0.47 |
- |
- |
|
|
FY·H3Cr13 |
- |
H3Cr13 |
0.330 |
0.66 |
0.57 |
13.20 |
0.31 |
- |
- |
|
|
品名 |
熔敷金屬機械性能之一例 |
主要特征及用途 |
||
|
TIG |
MIG |
抗拉MPa |
延伸率% |
|
|
FY·307 |
612 |
43 |
主要用于奧氏體錳鋼與碳鋼鍛件或鑄件的異種鋼焊接，具有良好的抗裂性能。 | |
|
FY·308 |
607 |
41 |
用于18Cr-8Ni鋼焊接，焊縫美觀，抗裂性好，電弧穩定。 | |
|
FY·308L |
575 |
42 |
用于18Cr-8Ni鋼焊接，比MIG308更耐腐蝕。 | |
|
FY·309 |
607 |
40 |
用于22Cr-12Ni鋼焊接，異種材料焊接用，耐熱耐蝕性好，電弧穩定，焊縫美觀。 | |
|
FY·309L |
590 |
43 |
異材焊接用，耐熱耐蝕性佳，低碳不銹鋼的焊接及耐熱鋼13Cr、18Cr鋼或異種金屬焊接。 | |
|
FY·309Si |
565 |
32 |
高Si-低C-22Cr-12Ni鋼用，其它同MIG309L。 | |
|
FY·310 |
607 |
41 |
25Cr-20Ni鋼用，比MIG309、MIG309L更適合種金屬焊接和自硬性高的合金鋼和高碳鋼的連接，異材焊接用。 | |
|
FY·316 |
576 |
38 |
18Cr-12Ni-2.5Mo(SUS316)鋼的焊接用，電弧穩定，焊道美觀。 | |
|
FY·316L |
565 |
41 |
低C-18Cr-12Ni-2.5Mo鋼用，比MIG316更耐腐蝕。 | |
|
FY·316LSi |
562 |
31 |
高Si-低C-18Cr-12Ni-2.5Mo鋼用，其它同MIG316L。 | |
|
FY·317 |
598 |
42 |
18Cr-12Ni-3.5Mo鋼用，Mo含量較高，對硫酸、亞硫酸等非氧化性及有機酸有優良的耐蝕性，其耐孔蝕性及耐熱性甚佳，適用重要化學容器的焊接 | |
|
FY·317L |
568 |
42 |
低C-18Cr-12Ni-3.5Mo鋼用，低碳高鉬，防止粒間腐蝕，焊接后免熱處理，高溫強度大，為抗硫酸、亞硫酸及有機酸的抗蝕專用焊絲。 | |
|
FY·321 |
562 |
39 |
20Cr-10Ni-Ti鋼用，由于Ti的加入，大大提高了抗晶間腐蝕的能力。 | |
|
FY·347 |
617 |
41 |
18Cr-9Ni-Ti鋼用，添加Nb使其熔敷金屬抗粒間腐蝕性增加，高溫強度好，特別適用于耐熱鋼的焊接。 | |
|
FY·410 |
510 |
25 |
13Cr鋼用，熔敷金屬為13Cr，硬化性大，在高溫下有優異的耐氧化性，和耐腐蝕性，適用于AISI410或420的焊接。 | |
|
FY·430 |
585 |
36 |
17Cr鋼用，特別適用于硝酸容器之焊接。 | |