產(chǎn)品介紹
|
Designation acc. to EN 573-3 |
Abbreviation |
State |
Mechanical Properties |
||||
|
Rm (MPa) |
Rp0,2 (MPa) |
A5 (%) |
|||||
|
EN AW-1050A |
EN AW - Al 99,5 |
Soft annealed |
70 |
45 |
40 |
||
|
Impact extruded |
130 |
110 |
6 |
||||
|
EN AW-1070A |
EN AW - Al 99,7 |
Soft annealed |
60 |
18 |
40 |
||
|
Impact extruded |
120 |
100 |
4 |
||||
|
EN AW-1200 |
EN AW - Al 99,0 |
Soft annealed |
70 |
45 |
40 |
||
|
Impact extruded |
130 |
110 |
6 |
||||
|
EN AW-2017A |
EN AW - AlCu4MgSi |
Solution annealed and naturally aged |
400 |
350 |
10 |
||
|
EN AW-5005A |
EN AW - AlMn1 |
Soft annealed |
90 |
35 |
24 |
||
|
Impact extruded |
170 |
145 |
4 |
||||
|
EN AW-5754 |
EN AW - AlMg3 |
Soft annealed |
190 |
80 |
20 |
||
|
Impact extruded |
265 |
215 |
4 |
||||
|
EN AW-6060 |
EN AW – AlMgSi |
Solution annealed and artificially aged |
245 |
195 |
10 |
||
|
EN AW-6061 |
EN AW - AlMg1SiCu |
Impact extruded |
|||||
|
Solution annealed and artificially aged |
|||||||
|
EN AW-6082 |
EN AW - Al Si1MgMn |
Impact extruded |
190 |
170 |
4 |
||
|
Solution annealed and artificially aged |
310 |
260 |
10 |
||||
|
EN AW-7020 |
EN AW - |
Solution annealed and artificially aged |
350 |
290 |
10 |
||
|
EN AW-7022 |
|
Solution annealed and artificially aged |
500 |
450 |
7 |
||
|
|
|||||||
4047鋁合金化學成分
鋁AL:余量
鋅Zn:≤0.20
錳Mn:≤0.15
鎂Mg:≤0.10
鐵Fe:≤0.8
硅Si:11.0-13.0
鈦Ti:/
鉻Cr:/
銅Cu:≤0.30
其它:單個:≤0.05
合計:≤0.15
抗拉強度135-155MPa，延伸率2-4%，布氏硬度50HBS
4000系鋁合金(Al-Si系)典型代表為4043、4343鋁合金，專門做為焊接材料。
表面質(zhì)量要求：
1、表面不允許有裂紋、腐蝕斑點和硝鹽痕跡。
2、表面上允許有深度不超過缺陷所在部位壁厚公稱尺寸8%的起皮、氣泡、表面粗超和局部機械損傷，但缺陷最大深度不能超過0.5mm,缺陷總面積不超過板材總面積的5%。
3、允許供貨方沿型材縱向打光至表面光滑。
4、其他要求：有需求方和供貨方自己擬定。
標準：
鋁板帶國家標準(GB/T 3880-2006)，適用于鋁合金板帶材料的統(tǒng)一標準。