特 性
|
可直接在鑄鐵上施焊,對于抗冷沖壓的金屬間磨耗非常有效.焊金第一層為奧氏體組織,從第二層開始為馬氏體組織抗磨耗性好. Can directly in the iron welding process, to make cold stamping metal abrasion very effective. Welding between the first layer of gold for austenitic group, second start martensite organization for good abrasion resistanceHRC46~52
|
|
用 途
|
球墨鑄鐵,火焰淬火鑄鐵,合金鑄鐵的直接堆焊. Ductile iron, flame hardening, alloy iron direct hardfacing.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠ 5.0￠
|
|
特 性
|
可直接在鑄鐵上施焊,對于抗冷沖壓的金屬間磨耗非常有效.焊金第一層為奧氏體組織,從第二層開始為馬氏體組織,抗磨耗沖壓性能優良. Can directly in the iron welding process, to make cold stamping metal abrasion very effective. Welding between the first layer of gold for austenitic group, second began to martensitic organization, abrasion resistance stamping excellent performance
|
|
用 途
|
主要用于各種淬火后鑄鐵的刃口修補焊接. Mainly used for various hardened iron blade repair welding.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠ 5.0￠
|
|
特 性
|
有良好的抗拉強度和延伸率 硬度HB-160. Have good tensile strength and elongation hardness HB - 160.
|
|
用 途
|
用于各種鑄鐵 合金鑄鐵 鋼與鑄鋼的焊接. For all kinds of iron alloy steel and cast iron welding.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠ 5.0￠
|
|
特 性
|
用于不同鑄鐵焊接時焊層能最大要求的滿足其顏色匹配,抗拉強度和延展性優良. Used for welding of different iron welding layer can satisfy the requirements of color matching, tensile strength and ductility.
|
|
用 途
|
焊補灰口鑄鐵,球墨鑄鐵. Weld-repair grey cast iron, ductile iron
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠ 5.0￠
|
|
特 性
|
高鉻成份,焊金具有高拉力,高韌性 HB-280. High chrome component, high strength, welding gold high toughness HB - 280.
|
|
用 途
|
鑄鋼模硬面制做打底緩沖層,裂縫敏感度較高的特種鋼接合襯焊使用. Cast steel hardfaced making render buffer layer, crack sensitive use of special steel lining welding joints.
|
|
規 格
|
2.6￠ 3.2￠
|
|
特 性
|
對沖壓模的金屬磨耗非常有效,焊金第一次為奧氏體組織,第二層為高硬度的馬氏體組織.火焰淬火鋼也可以直接堆焊. The metal stamping mould for abrasion is very effective for the first time, welding gold austenitic organization, the second is the high hardness martensite steel quenching. Flame may also directly hardfacing.
|
|
用 途
|
直接堆焊各種鑄鐵材的模具. All sorts of cast iron material directly surfacing of mould.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠ 5.0￠
|
|
特 性
|
耐沖擊與金屬間磨耗,直接焊于熱處理后的Cr12MoV鋼上,可全位置焊接,硬度HRC52~57.
Impact resistance and metal abrasion, directly welded to the Cr12MoV after heat treatment, but the POSTTTION on the steel welding, hardness HRC52-57
|
|
用 途
|
汽車大型模具硬面制做,冷沖模刀口焊接Auto giant mould making, cold die cutting hardfaced welding.
|
|
規 格
|
2.6￠ 3.2￠
|
|
特 性
|
熔敷金屬具有高硬度的馬氏體組織,耐磨耗耐沖擊性能優良,硬度HRC55~58. Deposited metal of martensite with high hardness, good abrasion resistance, impact resistant performance of hardness HRC55 ~ 58.
|
|
用 途
|
切模,沖壓模具的刃口焊材,也可以在碳鋼上堆焊制成新工具. Cutting, welding blade of stamping mould, also can be made in the new tool steel #.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|
|
特 性
|
高鉻成份,耐磨耗耐龜裂性能優良,焊后硬度較高,機械加工困難. High chrome component, abrasion resistance, resistance to crack excellent performance after welding, machining difficulty high hardness.
|
|
用 途
|
淬火硬化模具鋼刃口的修補,適用于SKD11合金工具鋼,淬火后的模具鋼修補. Quench hardened steel blade of repair, applicable to SKD11 alloy steel, alloy after quenching repair.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|
|
特 性
|
Cr Mo W V多元合金鋼耐磨堆焊材料,通過熱處理可調整堆焊金屬的硬度,耐熱到550℃.
Cr Mo w. v. multivariate alloy wear-resistant overlaying welding materials, heat treatment can be adjusted by the hardness and resistance buttering metal 550 degrees Celsius.
|
|
用 途
|
用于堆焊冷作熱作工具,模具.如壓鑄模具,鍛造工具 熱修整工具和冷切刀,可堆焊在低合金鋼上制成工具. Used for surfacing cold ReZuo tool, die casting die forging. Such as heat, cold and tool grinding tools, cutting knife can be made in the low alloy steel # tools.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|
|
特 性
|
中硬度鋼焊條HRC45~48 Hardness steel electrode in HRC45 ~ 48
|
|
用 途
|
適用于汽車模具,熱坯模,鑄鋼模耐中高溫沖擊磨耗之機件延壓部分的修補,焊層可加工. Applicable to auto mould casting mould casting, heat resistant steel, high impact abrasion of the drawing and pressing machine, welding parts repair coating can be processed.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|
|
特 性
|
高度耐熱耐磨耗,540℃高溫依然可保持52~54HRC. High abrasion resistance, heat 1,000-degree still can keep 54HRC - 52.
|
|
用 途
|
用于耐熱耐磨耗硬度要求很高的鍛模或錘鍛模刃口修復.更適用于H13等熱作模具局部和型腔修復. For high hardness resistant abrasion resistance of blade forging hammer forging or repair H13 etc. More suitable for ReZuo mold cavity and local repair.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|
|
特 性
|
熔敷金屬為低碳合金 含Ni Cr Mo V 極具韌性,含Mo V 所以回火時抗軟化,反復冷卻加熱也能保持良好的耐熱性能. For low carbon deposited metal alloys containing Ni Cr Mo V extremely toughness, including Mo V so when the tempering softening, cooling heating can keep good heat resistance.
|
|
用 途
|
熱作鍛造模的修補,要求在500℃耐熱耐沖擊耐金屬間磨耗部分的堆焊. ReZuo forging repair, requirements of 500 degrees in heat resistant to abrasion resistance to impact between metal parts of the hardfacing.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|
|
特 性
|
專為修補困難的淬火硬化型模具鋼和修補硬化堆焊缺損部分的焊接而開發設計的鈦鈣性焊條,不須要高溫預熱即可堆焊. Designed for repairing difficult quench hardened steel type and repair the defect of hardening surfacing welding and part of the design and development of titanium rod, don't need calcium temperature preheating can hardfacing.
|
|
用 途
|
焊補沖壓模 鍛造模 工具鋼等淬火硬化后模具材料的修補. Progressive metal stamping mould forging weld-repair after quench hardened steel mold materials etc.
|
|
規 格
|
2.6￠ 3.2￠ 4.0￠
|